oxidation behavior.8,22 High-carbon steel may suffer from decarburization
It was also observed that the Fe-C alloys decarburized when oxidized at oxygen pressure of 0.013 atm, but no decarburization was detected when the samples were oxidized at 0.92 atm.
Decarburization was significant at 850C, which was consistent with the results of others,115,116,121 but no measurable carbon loss was detected at 700C and below, indicating that carbon rejected from the oxidation of iron either diffused into the alloy substrate or accumulated at the scale-alloy interface.
causing decarburization of the steel when the rate of carbon oxidation
Decarburization is normally observed above 700C,